Principal Properties & Application:
ALITA 1506 resin is a new pentanediol-based unsaturated polyester resin primarily derived from phthalic anhydride and neopentyl glycol. It has high viscosity and high reactivity. This high-performance resin thickens quickly, has good flowability, and exhibits excellent strength and toughness. ALITA 1506 resin is suitable for general SMC/BMC (Sheet Molding Compound/Bulk Molding Compound) products, making it an ideal choice for compression molding resin applications. This fiber-reinforced polymer resin ensures superior mechanical properties, making it perfect for structural molding in various industrial components and automotive parts.
Liquid resin technical indicators:
| Item | Scope | Unit | Test Method |
| Exterior | light yellow transparent liquid | – | – |
| acid value | 17-25 | mgKOH/g | GB/T 2895-2008 |
| Viscosity, 25℃ | 1.2-1.8 | Pa.s | GB/T 7193-2008 |
| solid content | 64-70 | % | GB/T 7193-2008 |
| SPI-GT(80℃) | 5-10 | min | ALITA-D-DB001 |
Note: When testing the cure performance of SPI (Structural Polyurethane Injection) system, the curing agent used is Enox BPO-50F with a dosage of 2%.
Physical properties of the casting (for reference only):
| Item | Typical Value | Unit | Test Method |
| Exterior | Casting without defects | – | – |
| Barcol hardness | 45 | – | GB/T 3854-2005 |
| Heat distortion temperature | 75 | ℃ | GB/T 1634-2004 |
| Elongation at break | 2.5 | % | GB/T 2567-2008 |
| Tensile Strength | 68 | Mpa | GB/T 2567-2008 |
| Tensile modulus | 3150 | Mpa | GB/T 2567-2008 |
| Bending strength | 125 | Mpa | GB/T 2567-2008 |
| Flexural modulus of elasticity | 3750 | Mpa | GB/T 2567-2008 |
Note:
The casting fabrication method is conducted in accordance with GB/T 8237-2005. The curing system consists of a promoter (0.6% Co Naph) and a curing agent (Butanox M-50: 1.0%).
The post-casting treatment involves subjecting the castings to room temperature for 24 hours, followed by heating at 60°C for 3 hours, and finally at 120°C for 1 hour.
Usage instructions:
-
- ALITA 1506 resin does not contain wax, promoters, or thixotropic agents.
-
- To ensure the storage stability of SMC/BMC materials, stabilizers should be added appropriately during production.
Handling and Storage:
This resin contains ingredients which could be harmful if mishandled. Contact with skin and eyes should be avoided and necessary protective equipment and clothing should be worn.
Drums – It is highly recommended that all material is stored at stable temperatures below 25°C (77°F). Avoid exposure to heat sources such as direct sunlight or steam pipes. To avoid contamination of product with water, do not store outdoors. Keep sealed to prevent moisture pick-up and monomer loss. Rotate stock.
We provide small samples free of charge, but you will need to cover the shipping costs.
We have our own technical department. After you test the sample, please provide us with your detailed requirements. We can adjust the resin accordingly to enhance the properties of your finished products.
Honestly, it depends on the quantity. We will do our best to create a production plan based on your estimated time of arrival (ETA).
For the first trial order, we require 100% payment upfront. For subsequent orders, we ask for 30% payment in advance and 70% payment after the buyer receives the B/L copy. We also accept L/C if needed.
English 
Vietnamese 
Thai 
Spanish 
Indonesian 
Malay 
Russian